Search for: All records

Within the linear regime of mechanical and electrical responses, it is commonly accepted that direct and converse piezoelectric coefficients should be the same. However, we observed a consistently higher converse d31 (∼54 pm/V) than the direct d31 (∼42 pC/N) for a quenched, stretched, annealed, and electrically poled poly(vinylidene fluoride-co-trifluorethylene) [P(VDF-TrFE)] 52/48 mol.% sample (abbreviated as coP-52/48QSAP). On the contrary, the direct and converse d31 values were the same for coP-65/35QSAP and coP-55/45QSAP. Small-angle X-ray scattering results showed that coP-52/48QSAP had a higher amount of relaxor-like secondary crystals (SCs) in the oriented amorphous fraction (OAF) (SCOAF) than coP-55/45QSAP and coP-65/35QSAP. To explain the experimental observation, we performed molecular dynamics (MD) simulation of the pure PVDF (without TrFE) to estimate direct and converse piezoelectricity for the PVDF OAF. Based on the MD simulation, the direct d31 had a plateau value around 350 pC/N for the transverse (i.e., along the chain direction) strain up to 1 %, whereas the simulated converse d31 could be lower (for electric field E < 0.8 MV/m), equal (for E = 0.8 MV/m), or higher (for E > 0.8 MV/m) than the direct d31, depending on the poling electric field. From the MD simulation, both mechano-electrostriction and electrostatic interaction were identified in the OAF as the driving force for enhanced piezoelectricity in ferroelectric PVDF. When ferroelectric domains were formed in the OAF by electric poling, the simulated converse d31 became higher than the direct d31. Combining both experimental and MD simulation results, the higher converse d31 than direct d31 for coP-52/48QSAP was understood qualitatively. 

Current research on ferroelectric polymers centers predominantly on poly(vinylidene fluoride) (PVDF)–based fluoropolymers because of their superior performance. However, they are considered “forever chemicals” with environmental concerns. We describe a family of rationally designed fluorine-free ferroelectric polymers, featuring a polyoxypropylene main chain and disulfonyl alkyl side chains with a C3 spacer: −SO₂CH₂CHRCH₂SO₂− (R = −H or −CH₃). Both experimental and simulation results demonstrate that strong dipole-dipole interactions between neighboring disulfonyl groups induce ferroelectric ordering in the condensed state, which can be tailored by changing the R group: ferroelectric for R = −H or relaxor ferroelectric for R = −CH₃. At low electric fields, the relaxor polymer exhibits electroactuation and electrocaloric performance comparable with those of state-of-the-art PVDF-based tetrapolymers. 

Polymer piezoelectrics hold great potential for energy harvesting and wearable electronics. Efforts have been dedicated to enhancing piezoelectric coefficients and thermostability for several decades, but most of these have not been successful. In this report, we demonstrate a straightforward way to achieve high piezoelectric coefficients and output voltages while maintaining high thermostability at temperatures over 110 °C. Poly(vinylidene fluoride-co-trifluoroethylene) [P(VDF-TrFE)] 80/20 mol.% nanofiber mats (made by electrospinning) with extremely high crystallinity and Curie temperatures were obtained via a two-step annealing process, from which large ferroelectric domains were formed in extended-chain crystals. After corona poling using water, which is a high dielectric constant medium, giant piezoelectricity (apparent d33 = 1045 ± 20 pC/N) and high output voltages (29.9 ± 0.5 V) were achieved. It is found that the dimensional effect induced significant polarization changes, which is the key requirement for piezoelectricity. Our finding in this work paves a way to further improve high-performance polymer piezoelectrics. 

Abstract Despite extensive research on piezoelectric polymers since the discovery of piezoelectric poly(vinylidene fluoride) (PVDF) in 1969, the fundamental physics of polymer piezoelectricity has remained elusive. Based on the classic principle of piezoelectricity, polymer piezoelectricity should originate from the polar crystalline phase. Surprisingly, the crystal contribution to the piezoelectric strain coefficientd₃₁is determined to be less than 10%, primarily owing to the difficulty in changing the molecular bond lengths and bond angles. Instead, >85% contribution is from Poisson's ratio, which is closely related to the oriented amorphous fraction (OAF) in uniaxially stretched films of semicrystalline ferroelectric (FE) polymers. In this perspective, the semicrystalline structure–piezoelectric property relationship is revealed using PVDF‐based FE polymers as a model system. In melt‐processed FE polymers, the OAF is often present and links the crystalline lamellae to the isotropic amorphous fraction. Molecular dynamics simulations demonstrate that the electrostrictive conformation transformation of the OAF chains induces a polarization change upon the application of either a stress (the direct piezoelectric effect) or an electric field (the converse piezoelectric effect). Meanwhile, relaxor‐like secondary crystals in OAF (SC_OAF), which are favored to grow in the extended‐chain crystal (ECC) structure, can further enhance the piezoelectricity. However, the ECC structure is difficult to achieve in PVDF homopolymers without high‐pressure crystallization. We have discovered that high‐power ultrasonication can effectively induce SC_OAFin PVDF homopolymers to improve its piezoelectric performance. Finally, we envision that the electrostrictive OAF mechanism should also be applicable for other FE polymers such as odd‐numbered nylons and piezoelectric biopolymers. 

Among all ferroelectric polymers, poly(vinylidene fluoride) (PVDF)-based polymers exhibit the best piezoelectric properties and thus are promising for sensors, actuators, and energy harvesters in flexible/wearable electronics and soft robotics. Despite decades of research effort, the structure-property relationship is still unclear for ferroelectric polymers, and their piezoelectric performance is often limited to ~30 pC/N. In this study, we report the effects of chemical defects [i.e., the head-to-head and tail-to-tail (HHTT) sequence] and high-power ultrasonication on the piezoelectric performance of PVDF. Two PVDF homopolymers with different HHTT contents were studied. The PVDF with a lower HHTT content (4.3%) exhibited a higher melting temperature (Tm, denoted as HMT), whereas that with a higher HHTT content (5.9%) exhibited a lower Tm (denoted as LMT). In addition to the primary crystals (PCs) and the isotropic amorphous fraction, wide-angle X-ray diffraction also suggested the presence of the oriented amorphous fraction (OAF) and secondary crystals (SCs), which are important in enhancing the piezoelectricity for PVDF. Intriguingly, the LMT PVDF exhibited higher piezoelectric performance than the HMT PVDF, because it had a higher OAF/SC content. In addition, high-power ultrasonication was shown to effectively break relaxor-like SCs off from the PCs, further enhancing the piezoelectric performance. That is, the inverse piezoelectric coefficient d31 reached as high as 76.2 pm/V at 65 °C for the ultrasonicated LMT PVDF. The insight from this study will enable us to design better piezoelectric PVDF polymers for practical electromechanical applications. 

We explore structural correlations of strongly asymmetric mixtures of binary charged colloids within the primitive model of electrolytes considering large charge and size ratios of 10 and higher. Using computer simulations with explicit microions, we obtain the partial pair correlation functions between the like-charged colloidal macroions. Interestingly the big–small correlation peak amplitude is smaller than that of the big–big and small–small macroion correlation peaks, which is unfamiliar for additive repulsive interactions. Extracting optimal effective microion-averaged pair interactions between the macroions, we find that on top of non-additive Yukawa-like repulsions an additional shifted Gaussian attractive potential between the small macroions is needed to accurately reproduce their correct pair correlations. For small Coulomb couplings, the behavior is reproduced in a coarse-grained theory with microion-averaged effective interactions between the macroions. However, the accuracy of the theory deteriorates with increasing Coulomb coupling. We emphasize the relevance of entropic interactions exerted by the microions on the macroions. Our results are experimentally verifiable in binary mixtures of micron-sized colloids and like-charge nanoparticles. 

Although high piezoelectric coefficients have recently been observed in poly(vinylidene fluoride- co -trifluoroethylene) [P(VDF-TrFE)] random copolymers, they have low Curie temperatures, which makes their piezoelectricity thermally unstable. It has been challenging to achieve high piezoelectric performance from the more thermally stable PVDF homopolymer. In this report, we describe how high-power ultrasonic processing was used to induce a hard-to-soft piezoelectric transition and improve the piezoelectric coefficient d 31 in neat PVDF. After high-power ultrasonication for 20 min, a uniaxially stretched and poled PVDF film exhibited a high d 31 of 50.2 ± 1.7 pm V −1 at room temperature. Upon heating to 65 °C, the d 31 increased to a maximum value of 76.2 ± 1.2 pm V −1 , and the high piezoelectric performance persisted up to 110 °C. The enhanced piezoelectricity was attributed to the relaxor-like secondary crystals in the oriented amorphous fraction, broken off from the primary crystals by ultrasonication, as suggested by differential scanning calorimetry and broadband dielectric spectroscopy studies. 

Abstract Piezoelectric polymers hold great potential for various electromechanical applications, but only show low performance, with | d 33  | < 30 pC/N. We prepare a highly piezoelectric polymer ( d 33  = −62 pC/N) based on a biaxially oriented poly(vinylidene fluoride) (BOPVDF, crystallinity = 0.52). After unidirectional poling, macroscopically aligned samples with pure β crystals are achieved, which show a high spontaneous polarization ( P s ) of 140 mC/m 2 . Given the theoretical limit of P s,β  = 188 mC/m 2 for the neat β crystal, the high P s cannot be explained by the crystalline-amorphous two-phase model (i.e., P s,β  = 270 mC/m 2 ). Instead, we deduce that a significant amount (at least 0.25) of an oriented amorphous fraction (OAF) must be present between these two phases. Experimental data suggest that the mobile OAF resulted in the negative and high d 33 for the poled BOPVDF. The plausibility of this conclusion is supported by molecular dynamics simulations.